Name: LOCTITE 603
Brand: Henkel Corporation
SKU: LOCTITE 603

Main features

Low-Viscosity Cylindrical Component Retaining
High-Strength Steel Component Retention
Shock-and-Vibration Assembly Retention

Product Description

LOCTITE 603 is a one-component, low-viscosity urethane methacrylate retaining compound for close-fitting cylindrical metal assemblies. Its anaerobic cure develops when confined without air between mating metal surfaces, making it suited to retaining bearings and bushings in housings where consistently clean surfaces cannot always be assured. After 24 hours at 22 deg C, compressive shear strength on steel pins and collars is at least 22.5 N/mm^2 under ISO 10123. The cured compound also prevents loosening and leakage caused by shock and vibration.

Key features

Low-viscosity retention: One-component liquid for close-fitting cylindrical metal interfaces.
Anaerobic metal cure: Cures when confined without air between close-fitting metal surfaces.
Steel compressive shear strength: At least 22.5 N/mm^2 compressive shear after 24 hours at 22 deg C on steel pins and collars under ISO 10123.

Applications

Retaining cylindrical assemblies such as bearings, bushings and shafts.

TDS, SDS & Technical Documents

Technical Specifications

General Properties

Appearance

Green liquid

Chemistry Type

Urethane methacrylate

Specific Gravity

1.1

Physical Properties

Viscosity

100 to 150 mPa.s

Other Properties

Storage Temperature

8°C to 21 °C

Additional Information

Technical properties

As supplied

Property	Value	Unit	Method / condition
Specific gravity	1.1		25 deg C
Viscosity	100 to 150	mPa s	Brookfield RVT; spindle 1; 20 rpm; 25 deg C
Viscosity	90 to 180	mPa s	EN 12092-MV; 25 deg C; 277 s^-1 shear rate; after 180 seconds