LOCTITE LB 8034
Harmonization Code : 3403.19 | Lubricating Preparations (With 70% or More Petroleum Oils) For Automotive and Other Uses
Main features
- NLGI 2 PAO Lubrication
- 0.11% Evaporation Loss
- 400 kgf Four-Ball Weld Point
Product Description
LOCTITE LB 8034 is a one-component, non-curing NLGI Grade 2 grease with synthetic polyalphaolefin (PAO) base stocks and a calcium sulfonate additive. It lubricates machine parts and equipment, acts as a release agent on gaskets or seals, and can form a protective anti-rust film. Typical test data include 0.11% evaporation loss after 22 hours at 100 deg C by ASTM D972, a 0.42 mm four-ball wear scar by ASTM D2266, and a 400 kgf weld point by ASTM D2596. The supplied grease has specific gravity 0.95 to 1.05 and NLGI Class 2 consistency.
Key features
- PAO NLGI 2 Grease: A calcium sulfonate additive complements synthetic PAO base stocks in a non-curing grease.
- 0.11% Evaporation Loss: ASTM D972 result after 22 hours at 100 deg C.
- 400 kgf Weld Point: ASTM D2596 four-ball EP weld point; load-wear index is 53.2.
Applications
Machine-part and equipment lubrication, gasket and seal release, and protective anti-rust film use.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Other Properties
Electrical Properties
Additional Information
As supplied
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Chemical type | Polyalphaolefin | Base oil | |
| Specific gravity | 0.95 to 1.05 | 25 deg C | |
| NLGI class | 2 | ISO 6743-99 | |
| Penetration | >=290 | 1/10 mm | ISO 2137 |
| Drop point | >=318 | deg C | ISO 2176 |
In service
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Low-temperature torque | 0.37 start / 0.05 after 1 h | N m | ASTM D1478, -40 deg C |
| Evaporation loss | 0.11 | % | ASTM D972, 22 h at 100 deg C |
| Cone-bleed oil separation | 0.2 | % wt. loss | ASTM D6184, 100 deg C |
| Salt-fog corrosion | >350 | h | ASTM B117 |
| Water resistance | 0.57 | % | ASTM D1264, 80 deg C |
| Four-ball wear scar | 0.42 | mm | ASTM D2266 |
| Load-wear index | 53.2 | kgf | ASTM D2596 |
| Weld point | 400 | kgf | ASTM D2596 |