Name: LOCTITE PC7363
Brand: Henkel Corporation
SKU: LOCTITE PC7363

Main features

Non-Sag Ceramic-Tile Bonding
60-Minute Working Time
34.5 N/mm^2 Aluminum Lap Shear

Product Description

LOCTITE PC 7363 is a two-component epoxy paste adhesive for ceramic-tile installation on horizontal and vertical surfaces. The white-to-grayish paste mixes at a 1:1 resin-to-hardener ratio by volume. At 25 deg C, working time is 60 minutes and cure time is 12 hours. Cured material reaches Shore D 88 hardness and 96.6 N/mm^2 compressive strength. Lap shear is 34.5 N/mm^2 on acid-etched aluminum at a 0.125 mm gap. Typical dry service temperature is -29 to 93 deg C.

Key features

Non-Sag Tile Bonding: The non-sag paste bonds ceramic tile on horizontal and vertical surfaces.
60-Minute Working Time: Working time is 60 minutes at 25 deg C before the 12-hour cure time at the same temperature.
34.5 N/mm^2 Aluminum Lap Shear: Lap shear is 34.5 N/mm^2 on acid-etched aluminum with a 0.125 mm gap by ISO 4587.

Applications

Ceramic-tile installation and bonding on horizontal and vertical surfaces.

TDS, SDS & Technical Documents

Technical Specifications

General Properties

Appearance

White to grayish paste

Chemistry Type

Epoxy

Mix Ratio

1:1

Additional Information

Technical properties

As supplied

Property	Value	Unit	Method / condition
Resin viscosity	1,800,000 to 2,700,000	mPa s	Brookfield RV, spindle TF, 2.5 rpm, 25 deg C
Resin weight per gallon	12.1 to 12.9	lb/gal	As supplied
Hardener weight per gallon	15.2 to 16.0	lb/gal	As supplied
Mix ratio by volume	1:1		Resin:hardener; volume basis
Working time	60	min	25 deg C
Cure time	12	h	25 deg C