LORD 2232
Harmonization Code : 3506.10.00.00 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg
Main features
- 425 cP Application Viscosity
- At Most 0.100 ohms/sq/mil Cured Resistivity
- 2- to 3-Second Solder Wetting
Product Description
LORD 2232 Silver Conductive Coating is a silver-bearing thermoplastic conductive coating designed primarily as an electrode solder base for tantalum capacitor terminations. It can be applied by dip or brush and has a typical viscosity of 425 cP at 25 deg C. Typical settling rate is at most 2 mm/hr. After drying at 80 deg C for 10 minutes and curing at 125 deg C for 15 minutes, typical resistivity is at most 0.100 ohms/sq/mil. Typical solder wetting is 2 to 3 seconds with 62Sn/36Pb/2Ag solder at 200 deg C.
Key features
- Application Rheology: Typical viscosity is 425 cP at 25 deg C using a Brookfield LVT, spindle 2 at 60 rpm.
- Electrical Conductivity: Typical cured resistivity is at most 0.100 ohms/sq/mil after drying at 80 deg C for 10 minutes and curing at 125 deg C for 15 minutes.
- Solderability: Typical solder wetting is 2 to 3 seconds with 62Sn/36Pb/2Ag solder at 200 deg C.
Applications
Tantalum capacitor electrode terminations, printed circuit board repair, and electromagnetic shielding applications.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Viscosity | 425 | cP | Typical at 25 deg C; Brookfield LVT; spindle 2; 60 rpm |
| Settling rate | At most 2 | mm/hr | Typical property |
| Shelf life | 6 | months | From date of shipment; stored at 25 deg C in original, unopened container |