LORD 360
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- 1:1 Equal-Volume Mixing
- 5-10 Minute Handling Strength
- Minimal-Sag Vertical Application
Product Description
LORD 360-A/360-B is an equal-mix, two-part epoxy adhesive system for bonding scuffed SMC, FRP, wood and plastics. The 1:1 volume mix has a typical 2-4 minute working time at 24 deg C and reaches handling strength in 5-10 minutes between 18 and 38 deg C. For general use, a 0.51-0.76 mm adhesive film is recommended, and the mixed material shows minimal sag on vertical or overhead surfaces. Full cure strength develops in approximately 24 hours at room temperature or in 20-30 minutes at 82 deg C.
Key features
- Equal-Ratio Mixing: Resin and hardener are mixed at a 1:1 ratio by volume.
- Assembly Handling: The mixed adhesive reaches handling strength in 5 to 10 minutes between 18 and 38 deg C.
- Vertical Application: The mixed paste shows minimal sag on vertical and overhead surfaces.
Applications
Scuffed SMC, FRP, wood and other plastics, including sign-assembly applications.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
Component values are shown separately; mix and timing values apply to the combined LORD 360-A/360-B system.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| LORD 360-A viscosity | 90,000-180,000 | cP | Typical; Brookfield HBF, Helipath, 5 rpm; 25 deg C |
| LORD 360-B viscosity | 40,000-180,000 | cP | Typical; Brookfield HBF, Helipath, 5 rpm; 25 deg C |
| LORD 360-A density | 1,438-1,618 | kg/m3 | Typical |
| LORD 360-B density | 1,019-1,138 | kg/m3 | Typical |
| Mix ratio | 1:1 | by volume | Resin to hardener |
| Working time | 2-4 | minutes | Typical; 54 g mass at 24 deg C |
| Time to handling strength | 5-10 | minutes | Typical; 18-38 deg C |
| Shelf life | 2 | years | Original unopened container at 16-27 deg C |