PERMABOND ES562
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- One-Part Heat-Cure Processing
- Self-Leveling Elevated-Temperature Flow
- 20 to 35 MPa Steel Shear
Product Description
PERMABOND ES562 is a single-component heat-cure epoxy adhesive for structural bonding of metals and composite materials. It is low viscosity and self-leveling, and it becomes free flowing at elevated cure temperature. Typical oven cure schedules include 60 minutes at 130 deg C, 45 minutes at 150 deg C or 20 minutes at 160 deg C; induction cure can be under 3 minutes. Typical cured shear strength is 20 to 35 MPa on steel and 14 to 27 MPa on aluminum under ISO 4587. The product is suited to assemblies that benefit from one-part handling, controlled heat cure and a rigid cured epoxy bond.
Key features
- One-Part Heat Cure: No component mixing is required before the thermal cure process.
- Self-Leveling Flow: The adhesive is low viscosity and free flowing at elevated cure temperature.
- High Cured Shear Strength: Typical ISO 4587 shear strength is 20 to 35 MPa on steel after cure.
Applications
Bonding metals and composite materials where a heat-cure single-part epoxy is suitable.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
Typical values; not for use in preparing specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Chemical composition | Epoxy resin | - | Uncured adhesive |
| Appearance | White | - | Uncured adhesive |
| Specific gravity | 1.2 | - | Typical, uncured adhesive |
Cured adhesive properties
Typical values; not for use in preparing specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Shear strength - steel | 20 to 35 | MPa | Typical, ISO 4587 |
| Shear strength - aluminum | 14 to 27 | MPa | Typical, ISO 4587 |
| Tensile strength | 40 | N/mm^2 | Typical, DIN 53504 |
| Hardness | 80 to 85 | Shore D | Typical, ISO 868 |
| Glass transition temperature | 115 | deg C | Typical, DSC |
| Thermal conductivity | 0.25 | W/(m K) | Typical, cured adhesive |