LOCTITE H8100
Harmonization Code : 3403.19 | Lubricating Preparations (With 70% or More Petroleum Oils) For Automotive and Other Uses
Main features
- Fast 18-Minute Steel Fixture
- High-Elongation Structural Acrylic
- 10:1 Non-Sag Mixing
Product Description
LOCTITE AA H8100 is a non-sag, two-part methacrylate structural adhesive mixed 10:1 by volume for room-temperature bonding of metals, plastics, and composites. The system has a 15-minute working time at 25 deg C and reaches fixture strength in 18 minutes on grit-blasted mild steel under ISO 4587. Its cured material has 20% elongation at break, Shore D 62 hardness, a typical Tg of 75 deg C, and lap shear strength of at least 19.31 N/mm^2 on steel after 24 hours at 22 deg C. The resin is yellow, the hardener is blue, and the mixed adhesive is green.
Key features
- Non-Sag Methacrylate Mixing: The two-part system uses a 10:1 by-volume mix ratio.
- Working and Fixture Times: Working time is 15 minutes at 25 deg C; fixture time is 18 minutes on grit-blasted mild steel.
- High-Elongation Cured Acrylic: Cured material reaches 20% elongation at break with Shore D 62 hardness.
Applications
Structural bonding of metals, plastics, and composite substrates.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Thermal Properties
Mechanical Properties
Other Properties
Additional Information
As-supplied / before-processing properties
Part A, Part B, and mixed-material values remain state-specific; the 10:1 mix ratio is by volume.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Mix ratio, Part A:Part B | 10:1 | - | By volume |
| Specific gravity, mixed | 0.97 | - | Typical; 25 deg C |
| Viscosity, mixed | 15,360 | mPa s | Typical; cone and plate CP50-1, 25 deg C, shear rate 50 s^-1 |
| Working time | 15 | minutes | Typical; 25 deg C, maximum time before assembly on steel, aluminum, and polyethylene |
| Fixture time | 18 | minutes | Typical; ISO 4587, grit-blasted mild steel |
After-processing / final-state properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Glass transition temperature | 75 | deg C | Typical; ISO 11359-2 |
| Shore hardness | 62 | Durometer D | Typical; ISO 868 |
| Elongation at break | 20 | % | Typical; ISO 527-2 |
| Tensile modulus | 770 | N/mm^2 | Typical; ISO 527-2 |
| Lap shear strength on steel | >=19.31 | N/mm^2 | Typical performance; ISO 4587, cured 24 hours at 22 deg C |