LORD 201/17
Harmonization Code : 3919.10.80 | Other self-adhesive plastic rolls not exceeding 20 cm wide.
Main features
- 10:1 Volume Mix Ratio
- 5- to 8-Minute Working Time
- 31.7 MPa 6061-T6 Aluminum Lap Shear
Product Description
LORD 201/Accelerator 17 is a two-part acrylic adhesive system for structural bonding of prepared or unprepared metals and plastics. LORD 201 is mixed with Accelerator 17 at a 10:1 volume ratio. At 24 deg C, the mixed system has a typical 5- to 8-minute working time and reaches handling strength in 12 to 16 minutes; complete cure takes 24 hours at room temperature. The adhesive is self-leveling and can be dispensed from handheld cartridges or meter/mix/dispense equipment. Typical 6061-T6 aluminum lap shear is 31.7 MPa after a 24 hr room-temperature cure with a 0.010 in film.
Key features
- System Mixing: LORD 201 and Accelerator 17 are mixed at 10:1 by volume.
- Mixed-System Work Time: Typical working time is 5 to 8 minutes at 24 deg C.
- Aluminum Lap Shear: Typical lap shear is 31.7 MPa on 6061-T6 aluminum after a 24 hr room-temperature cure with a 0.010 in film.
Applications
Structural bonding of metals, ceramics, and plastics, including prepared or unprepared metal surfaces and irregular shapes where self-leveling application is useful.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Additional Information
After-processing / final-state properties
Typical LORD 201/Accelerator 17 bond-performance data.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Lap shear - cold rolled steel SAE 1010 | 31.0 | MPa | ASTM D1002; MEK wipe; 24 hr at room temperature; 10:1 by volume; 0.010 in film |
| Lap shear - stainless steel | 27.6 | MPa | ASTM D1002; MEK wipe; 24 hr at room temperature; 10:1 by volume; 0.010 in film |
| Lap shear - aluminum 6061-T6 | 31.7 | MPa | ASTM D1002; MEK wipe; 24 hr at room temperature; 10:1 by volume; 0.010 in film |