LORD 406/17
Harmonization Code : 38159000 | Unspecified reaction initiators, accelerators, and catalytic preparations
Main features
- 10:1 Accelerator 17 Volume Mix
- 6-10 Minute Working Window
- 12-17 Minute Handling Strength
Product Description
LORD 406/Accelerator 17 is a two-part acrylic adhesive system for bonding prepared or unprepared metals and engineered plastics. LORD 406 is an off-white to tan paste with typical viscosity of 100,000-300,000 cP at 25 deg C. With Accelerator 17, the system mixes at 10:1 by volume or 9.33:1 by weight, has a 6-10 minute working time at 24 deg C, and reaches 60 psi handling strength in 12-17 minutes. Full cure requires 24 hours at 24 deg C. The mixed adhesive is non-sag for vertical and overhead application.
Key features
- System Mixing: LORD 406 and Accelerator 17 use a 10:1 adhesive-to-accelerator ratio by volume.
- Mixed-System Work Time: The mixed system has a typical working time of 6 to 10 minutes at 24 deg C.
- Vertical Application: The mixed adhesive remains in position on vertical and overhead surfaces.
Applications
Prepared or unprepared metals and engineered thermoplastics including polycarbonate, ABS and acrylics.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Mechanical Properties
Additional Information
As-supplied / before-processing properties
Component values apply to LORD 406; mix and timing values apply specifically to the LORD 406/Accelerator 17 system.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| LORD 406 viscosity | 100,000-300,000 | cP | Typical; Brookfield; 25 deg C |
| LORD 406 density | 1,090-1,162 | kg/m3 | Typical |
| Mix ratio | 10:1 | by volume | LORD 406 adhesive to Accelerator 17 |
| Mix ratio | 9.33:1 | by weight | LORD 406 adhesive to Accelerator 17 |
| Solids content | 100 | % | Typical; mixed system |
| Working time | 6-10 | minutes | Typical; mixed system at 24 deg C |
| Time to handling strength | 12-17 | minutes | Typical; 60 psi shear threshold at 24 deg C |
| Full cure time | 24 | hours | Typical; mixed system at 24 deg C |